P1L
|
|
|
|
|
|
|
|
Compressione |
Taglio |
| Codice/Code |
B |
H |
S |
L |
Pc |
ƒc |
Ne |
Pt |
ƒt |
Ne |
| 4035 |
40,0 |
35,0 |
8,0 |
1.000,0 |
2,5 |
1,42 |
798 |
0,85 |
4,6 |
442 |
| 5030 |
50,0 |
30,0 |
10,0 |
1.000,0 |
3,0 |
1,18 |
875 |
1,10 |
5,1 |
420 |
| 5035 |
50,0 |
35,0 |
10,0 |
1.000,0 |
3,0 |
1,35 |
817 |
1,10 |
5,8 |
394 |
| 5050 |
50,0 |
50,0 |
10,0 |
1.000,0 |
3,0 |
3,30 |
522 |
1,10 |
10,4 |
295 |
| 6060 |
60,0 |
60,0 |
10,0 |
1.000,0 |
3,5 |
4,70 |
438 |
1,20 |
14,2 |
252 |
| 7050 |
70,0 |
50,0 |
10,0 |
1.000,0 |
4,0 |
2,80 |
567 |
1,50 |
8,1 |
333 |
| 7060 |
70,0 |
60,0 |
10,0 |
1.000,0 |
4,0 |
4,50 |
447 |
1,50 |
12,0 |
274 |
| 10050 |
100,0 |
50,0 |
15,0 |
1.000,0 |
5,5 |
0,80 |
1063 |
2,50 |
6,1 |
384 |
| 10060 |
100,0 |
60,0 |
15,0 |
1.000,0 |
5,5 |
1,95 |
680 |
2,50 |
8,1 |
333 |
| 10080 |
100,0 |
80,0 |
15,0 |
1.000,0 |
5,5 |
5,60 |
401 |
2,50 |
12,9 |
264 |
| 15060 |
150,0 |
60,0 |
15,0 |
1.000,0 |
8,0 |
1,32 |
826 |
3,50 |
10,5 |
292 |
| 15080 |
150,0 |
80,0 |
15,0 |
1.000,0 |
8,0 |
3,10 |
539 |
3,50 |
12,4 |
269 |
| 150100 |
150,0 |
100,0 |
15,0 |
1.000,0 |
8,0 |
6,50 |
372 |
3,50 |
18,2 |
222 |
| Legenda: |
Pc = carico in daN/mm a compressione |
|
fc = freccia in mm a compressione |
|
ne = frequenza propria dell'antivibrante |
|
Pt = carico in daN/mm a taglio |
|
ft = freccia in mm a taglio |
|
NB. Tutti i valori indicati sono per elastomero con durezza di 50°
Sh.A, per le altre durezze utilizzare i fattori di correzione sotto indicati: |
|
Frequenza propria
45° Sh.A x 0,79
60° Sh.A x 1,15
70° Sh.A x 1,31 |
Freccia
45° Sh.A x 1,83
60° Sh.A x 0,82
70° Sh.A x 0,62 |
|
|